PVDF heat shrink tubing Product Specifications：
Local de origem: China
Brand Name: Yozonetech
Type: Insulator
Material:PVDF
Application:High Temperature
Rated Voltage:1kv
Tensile Strength:30MPA min
Product name:PVDF heat shrink tubing Kynar heat shrink tubes
Tensile strength:30 Mpa min
Operating temperature:-55 ~+150 °C
Elongation at break:150% min
Elongation at break after aging:100% min
Flammability:Flamable
shrink ratio:2:1
Supply Ability:10000 Meter/Meters per Day
Polyvinylidene Fluoride (PVDF) is a thin-wall heat shrinkable tube made from radiation-modified polyvinylidene fluoride. It is transparent, flame retardant, resistant to high temperatures, most oils, and chemicals, as well as being durable and cut-resistant. It is widely used for protecting welding points, terminals, and connecting cables that are exposed to high temperatures, industrial fuels, solvents, and chemical agents.
PVDF heat shrink tubing Product Features:
Shrink Ratio: 2:1
Minimum Shrink Temperature: ≥+135℃
Operating Temperature: -55℃ to +150℃
Flexible, corrosion-resistant, abrasion-resistant, and cut-resistant Environmental Standard: RoHS
Standard Colors: Transparent, Black.
| Desempenho | Desempenho | Index | Método de ensaio |
|---|---|---|---|
| Physical Performance | Tamanho | Customized | ASTM D 2671 |
| Longitudinal Length Change | -10%~+5% | ASTM D 2671 | |
| Tensile Strength | ≥24.1 MPa | ASTM D 2671 | |
| Alongamento na rutura | ≥300% | ASTM D 2671 | |
| Shrink Ratio | ≤40% | AMS-DTL-23053 | |
| Tangent Modulus | ≥172 MPa | ASTM D 2671 | |
| Densidade | ≤1.9 g/cm3 | ASTM D 2671 | |
| Low-Temperature Flexibility | No Cracks | AMS-DTL-23053(-55℃×4h) | |
| Thermal Shock | No Dripping, No Flowing, No Cracks | ASTM D 2671(250℃×4h) | |
| Tensile Strength after Heat Aging | ≥19.1 MPa | ASTM D 2671(225℃×168h) | |
| Elongation at Break after Heat Aging | ≥200% | ASTM D 2671(225℃×168h) | |
| Transparency StabilityIdentification | Markings Still Clear | AMS-DTL-23053(200℃×24h) | |
| Electrical Insulation Performance | Resistência dieléctrica | ≥15.7kV/mm | ASTM D 2671 |
| Volume Resistivity | ≥1012Ω ·cm | ASTM D 2671 | |
| Chemical Performance | Copper Corrosion | No Corrosion | ASTM D 2671(160℃×16h) |
| Flame Retardant | Self-extinguishing within 60s, Paper Flag Burning Degree | UL224 VW-1， ASTM D 2671 C法 |
|
| Water Absorption | ≤0.5% | ISO 846 B法, 23℃×24h | |
| Tensile Strength after Fungus Resistance | ≥24.1 MPa | ASTM D 2671 | |
| Elongation at Break after Fungus Resistance | ≥300% | ASTM D 2671 | |
| Dielectric Strength after Fungus Resistance | ≥15.7kV/mm | ASTM D 2671 | |
| Tensile Strength after Chemical Resistance | ≥13.8 MPa | ASTM D 2671 | |
| Elongation at Break after Chemical Resistance | ≥200% | ASTM D 2671 | |
| Dielectric Strength after Chemical Resistance | ≥15.7kV/mm | ASTM D 2671 |
| Tamanho | Product ID (mm) | Size after shrinking (mm) | Shape | Package m/roll | ||
|---|---|---|---|---|---|---|
| Inch | mm | ID | Wall thickness | |||
| 1/32 | Φ0.8 | ≥0.8 | ≤0.5 | 0.30±0. 10 | Redondo | 200 |
| 3/64 | Φ1.2 | ≥ 1.2 | ≤0.6 | 0.33±0. 10 | Redondo | 200 |
| 1/ 16 | Φ1.6 | ≥ 1.6 | ≤0.8 | 0.33±0. 10 | Redondo | 200 |
| 3/32 | Φ2.4 | ≥2.4 | ≤ 1.2 | 0.33±0. 10 | Redondo | 200 |
| 1/8 | Φ3.2 | ≥3.2 | ≤ 1.6 | 0.35±0. 10 | Redondo | 100 |
| 3/ 16 | Φ4.8 | ≥4.8 | ≤2.4 | 0.35±0. 10 | Redondo | 100 |
| 1/4 | Φ6.4 | ≥6.4 | ≤3.2 | 0.35±0. 10 | Flat | 100 |
| 3/8 | Φ9.5 | ≥9.5 | ≤4.8 | 0.38±0. 10 | Flat | 50 |
| 1/2 | Φ12.7 | ≥ 12.7 | ≤6.4 | 0.38±0. 10 | Flat | 50 |
| 5/8 | Φ15.0 | ≥ 15.0 | ≤7.5 | 0.40±0. 10 | Flat | 50 |
| 3/4 | Φ19. 1 | ≥ 19. 1 | ≤9.5 | 0.42±0. 10 | Flat | 50 |
| 1 | Φ25.4 | ≥25.4 | ≤ 12.7 | 0.42±0. 10 | Flat | 50 |
| 1- 1/2 | Φ38. 1 | ≥38. 1 | ≤ 19. 1 | 0.48±0. 10 | Flat | 50 |
175ºC PVDF heat shrink tube
Product Introduction: The 175℃ Polyvinylidene Fluoride Tubo termo-retrátil is made from radiation-modified polyvinylidene fluoride, offering transparency, flame retardancy, high-temperature resistance, resistance to most oils and chemicals, as well as durability and cut-resistant properties. Custom heat shrink tubing finds extensive applications in protecting welding points, terminals, and connecting cables that heat shrink tubing manufacturers are exposed to high temperatures, industrial fuels, solvents, and chemical agents.
PVDF heat shrink tubing Product Features:
Shrink Ratio: 2:1 Minimum Shrink
Temperature: ≥+175℃
Operating Temperature: -55℃ to +175℃
Flexible, corrosion-resistant, abrasion-resistant, and cut-resistant
Environmental Standard: RoHS
Standard Colors: Transparent, Black.
| Desempenho | Performance Index | Método de ensaio |
|---|---|---|
| Densidade | 1.78 g/cm³ | ASTM D791 |
| Tensile Strength | ≥30 MPa | ASTM D2671 |
| Alongamento na rutura | ≥ 150% | ASTM D2671 |
| Elongation at Break after Aging | ≥ 100% | 250C×168h |
| Volume Resistivity | ≥ 1014 Ω•cm | IEC 60093 |
| Flame Retardant | VW- 1 | UL224 |
| Cold Bend Flexibility | No cracks | -55C×4h |
| Thermal Shock | No cracks | 250C×4h |
| Copper Corrosion | No corrosion | 180C×168h |
| Copper Stabilization | Copper Stabilization | 180C×168h |
| Tamanho | Product size (mm) | Size after shrinking (mm) | Shape | Package m/roll | ||
|---|---|---|---|---|---|---|
| Inch | mm | ID | Wall thickness | |||
| 3/64 | Φ1.2 | ≥ 1.2 | ≤ 0.6 | 0.33±0. 10 | Redondo | 200 |
| 1/ 16 | Φ1.6 | ≥ 1.6 | ≤ 0.8 | 0.33±0. 10 | Redondo | 200 |
| 3/32 | Φ2.4 | ≥ 2.4 | ≤ 1.2 | 0.33±0. 10 | Redondo | 200 |
| 1/8 | Φ3.2 | ≥ 3.2 | ≤ 1.6 | 0.35±0. 10 | Redondo | 100 |
| 3/ 16 | Φ4.8 | ≥ 4.8 | ≤ 2.4 | 0.35±0. 10 | Redondo | 100 |
| 1/4 | Φ6.4 | ≥ 6.4 | ≤ 3.2 | 0.35±0. 10 | Flat | 100 |
| 3/8 | Φ9.5 | ≥ 9.5 | ≤ 4.8 | 0.38±0. 10 | Flat | 50 |
| 1/2 | Φ12.7 | ≥ 12.7 | ≤ 6.4 | 0.38±0. 10 | Flat | 50 |
| 5/8 | Φ15.0 | ≥ 15.0 | ≤ 7.5 | 0.40±0. 10 | Flat | 50 |
| 3/4 | Φ19.1 | ≥ 19.1 | ≤ 9.5 | 0.42±0. 10 | Flat | 50 |
| 1 | Φ25.4 | ≥ 25.4 | ≤ 12.7 | 0.42±0. 10 | Flat | 50 |
| 1- 1/2 | Φ38.1 | ≥ 38.1 | ≤ 19.1 | 0.48±0. 10 | Flat | 50 |